ASTM A0921_A0921M-93R22
Standard Specification for Steel Bars, Microalloy, Hot-Wrought, Special Quality, for Subsequent Hot Forging
| Označení normy: | ASTM A0921_A0921M-93R22 |
| Vydáno: | 01.03.2022 |
| Status: | Active |
| Počet stran: | 3 |
| Sekce: | 01.05 |
| Označení: | carbon steel bars; microalloyed steel; steel bars; |
| ASTM označení: | ASTM A921/A921M |
| Nahrazuje: | A0921_A0921M-93R16 |
This specification covers hot-wrought, special quality microalloyed carbon steel bars intended for use as hot forging stock. The bars shall be hot-wrought, as-wrought, unless thermal treatment is necessary to ensure cold shearability. The steel specimens shall be killed and shall conform to the fine grain size requirement. Heat analysis and product analysis shall be performed wherein the specimens shall conform to the required chemical compositions of vanadium, columbium, and molybdenum.
1.1 This specification covers hot-wrought, special quality microalloyed carbon steel bars intended for use as hot forging stock. The bars shall be hot-wrought, as-wrought, unless thermal treatment is necessary to ensure cold shearability.
1.2 The bars shall be furnished to chemical composition only. Chemical composition is based on standard carbon steel grades modified to include microalloying elements such as columbium (niobium), vanadium, or molybdenum. Desired mechanical properties are developed in the subsequent hot forging and controlled cooling operations.
1.3 Sections and sizes of bar steel available are covered in Specification A29/A29M.
1.4 Supplementary Requirements S1 to S6 are provided for use when additional controls or requirements are desired. These shall apply only when specified on the purchase order.
1.5 The values stated in either inch-pound units or SI units are to be regarded separately as standard. Within the text and tables, SI units are shown in brackets. The values stated in each system are not necessarily exact equivalents; therefore, to ensure conformance with the standard, each system shall be used independently of the other, and values from the two systems shall not be combined.
1.6 Unless the order specifies the applicable “M” specification designation, the material shall be furnished to the inch-pound units.
1.7 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.