Standard Specification for Zinc-Coated (Galvanized) Steel Core Wire for Use in Overhead Electrical Conductors
| Označení normy: | ASTM B0498_B0498M-22 |
| Vydáno: | 01.10.2022 |
| Status: | Active |
| Počet stran: | 4 |
| Sekce: | 02.03 |
| Označení: | coated steel wire; steel core wire; steel wire; zinc-coated steel wire; |
| ASTM označení: | ASTM B498/B498M |
| Nahrazuje: | B0498_B0498M-19 |
This specification covers round, zinc-coated (galvanized), steel core wire with three classes of zinc coating used for mechanical reinforcement in the manufacture of aluminum conductors, steel-reinforced (ACSR). The wire is furnished in three classes of coating, namely: Class A, Class B, and Class C. The base metal shall be steel produced by the open-hearth, electric-furnace, or basic-oxygen process. The wire shall be cold drawn and coated with zinc to produce the desired properties and the the slab zinc used for coating shall be high-grade or better. The steel shall conform to the chemical composition requirements prescribed for carbon, manganese, phosphorus, sulfur, and silicon, as determined by chemical analysis. The following tests shall be performed: (1) tensile test to determine the mechanical properties such as ultimate tensile strength, elongation, and stress at extension, (2) wrap test, (3) coating test to determine conformity to the specified diameter and area density requirements, and (4) coating adherence test. Requirements for joints which may be made by electric butt-weld or flash-welding are detailed. The density and resistivity of galvanized steel wire are prescribed for the purposes of calculating mass per unit length, cross-sections, and so forth.
1.1 This specification covers round, zinc-coated, steel core wire with two classes of zinc coating for use in overhead electrical conductors.
1.2 This specification covers wire of diameter from 0.0500 to 0.1900 in. or 1.27 to 4.82 mm, inclusive.
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.